Untersuchung der UVC-Bestrahlung als Oberflächenvorbehandlungsmethode von Polycarbonaten zur Erzeugung einer Verbundhaftung zu Flüssigsilikonkautschuken

Hartung, Michael

dc.date.accessioned	2023-06-15T13:56:52Z
dc.date.available	2023-06-15T13:56:52Z
dc.date.issued	2023
dc.identifier	doi:10.17170/kobra-202304277905
dc.identifier.uri	http://hdl.handle.net/123456789/14830
dc.description	Zugleich: Dissertation, Universität Kassel, 2023
dc.language.iso	ger
dc.publisher	kassel university press
dc.rights	Namensnennung - Weitergabe unter gleichen Bedingungen 4.0 International	*
dc.rights.uri	http://creativecommons.org/licenses/by-sa/4.0/	*
dc.subject	Hart/Weich-Verbunde	ger
dc.subject	Silikonelastomere	ger
dc.subject	Oberflächenvorbehandlung Mehrkomponentenspritzgießen	ger
dc.subject	Adhäsion	ger
dc.subject.ddc	600
dc.title	Untersuchung der UVC-Bestrahlung als Oberflächenvorbehandlungsmethode von Polycarbonaten zur Erzeugung einer Verbundhaftung zu Flüssigsilikonkautschuken	ger
dc.type	Buch
dcterms.abstract	Das Mehrkomponentenspritzgießen ermöglicht die wirtschaftliche Herstellung von funktionenintegrierten Hart/Weich-Verbunden aus Thermoplasten und Flüssigsilikonkautschuken. Häufig stellt jedoch die unzureichende Haftung beider Komponenten zueinander eine Herausforderung dar. Insbesondere für Polycarbonat als Hartkomponente ist die Auswahl an haftungsmodifizierten Flüssigsilikonkautschuken eingeschränkt. Abhilfe kann hier eine Oberflächenvorbehandlung schaffen, um gezielt funktionelle Gruppen in die Oberfläche einzubringen, welche die Polarität erhöhen und als Ankopplungspunkte für den Haftvermittler dienen. In dieser Arbeit wurde die UVC/Ozon-Bestrahlung von BPA-Polycarbonat zur Haftvermittlung zu selbsthaftenden Flüssigsilikonkautschuken hinsichtlich Beständigkeit und Prozess-Eigenschafts-Korrelationen untersucht. Dabei konnte festgestellt werden, dass die Aktivierung bei Raumtemperatur für mindestens 36 Monate beständig ist. Temperaturen über 120°C und insbesondere Anwesenheit von Wasser wirken sich hingegen bereits nach wenigen Tagen schädigend aus. Vergleichbare Ergebnisse liegen für die Beständigkeit der Haftverbunde vor. Als maßgebliche Bedingung für die Erzeugung von kohäsivem Verbundversagen in der Weichkomponente konnte die Bestrahlungsdosis ermittelt werden. Dies erlaubt eine Übertragung der Ergebnisse auf abweichende Geometrien von Bauteilen und Strahlungsquellen sowie Bestrahlungsabständen bei Kenntnis der wirkenden Bestrahlungsstärke. Mithilfe von Photometern können diese Gegebenheiten messtechnisch einfach ermittelt werden. Oberflächenanalysen mittels Kontaktwinkel-, FTIR-ATR- und ToF-SIMS-Messungen zeigten, dass infolge der kurzzeitigen UVC/Ozon-Bestrahlung eine erhöhte Konzentration an sauerstoffhaltigen Verbindungen (insbesondere OH-Gruppen) in der Polycarbonatoberfläche erzeugt wird. Diese gehen aus Hauptkettenspaltungen sowie Photo-Fries-Umlagerungen bis in Tiefen von wenigen Mikrometern hervor. Die Entstehung dieser Verbindungen wird chemisch für den Effekt der Haftvermittlung verantwortlich gemacht. Die gewonnenen Ergebnisse tragen dazu bei, dass die UVC/Ozon-Bestrahlung zukünftig für die Herstellung von Polycarbonat/LSR-Verbunden genutzt werden kann. Durch eine einfache Integration in einen Mehrkomponentenspritzgießprozess sowie die Kenntnis zum Zusammenhang zwischen Bestrahlungsdosis und Haftung kann das Verfahren in Praxisanwendungen übertragen werden.	ger
dcterms.abstract	Multi-component injection molding enables the economical production of function integrated hard/soft composites made of thermoplastics and liquid silicone rubbers. Particularly for polycarbonate as a hard component, the choice of self-adhesive liquid silicone rubbers is limited. This can be improved by surface pretreatment. In addition to plasma and flame treatments, which are well established in practice, short-term UVC/ozone irradiation has proven to be extremely effective in achieving cohesive failure in the soft component under load, starting from no adhesion. In this work, UVC/ozone irradiation of polycarbonate for adhesion to self-adhesive liquid silicone rubbers was investigated with regard to the resistance of the activation and the adhesion bond as well as the dependencies of the adhesion in regard to the irradiation doses. It was found that the activation is stable at room temperature for at least 36 months. At temperatures above 120°C and especially in the presence of water, adhesion formation is no longer possible after a few days. Similar results are available for the durability of the composites. The irradiation dose was determined to be a decisive condition for the generation of high adhesion. This characterization allows the results to be transferred to different geometries of components and radiation sources as well as irradiation distances if the irradiance is known. These conditions can be easily determined with photometers. Surface analyses using contact angle, FTIR-ATR and ToF-SIMS measurements showed that an increased concentration of oxygen-containing compounds is introduced into the polycarbonate surface as a result of the short-term UVC/ozone irradiation. These arise from main chain scissions as well as Photo-Fries rearrangements down to depths of a few micrometers. The formation of these compounds is chemically responsible for the effect of adhesion promotion. The obtained results contribute to the future use of UVC/ozone irradiation for the production of polycarbonate/LSR composites. The process can be transferred to practical applications through simple integration into a multi-component injection molding process and knowledge of the relationship between irradiation dose and adhesion.	eng
dcterms.accessRights	open access
dcterms.creator	Hartung, Michael
dcterms.dateAccepted	2023-04-21
dc.contributor.corporatename	Kassel, Universität Kassel, Fachbereich Maschinenbau	ger
dc.contributor.referee	Heim, Hans-Peter (Prof. Dr.-Ing.)
dc.contributor.referee	Moritzer, Elmar (Prof. Dr.-Ing.)
dc.publisher.place	Kassel
dc.relation.isbn	978-3-7376-1115-2
dc.subject.swd	Oberflächenvorbereitung	ger
dc.subject.swd	Mehrkomponenten-Spritzgießen	ger
dc.subject.swd	Adhäsion	ger
dc.type.version	publishedVersion
dcterms.source.series	Schriftenreihe des Instituts für Werkstofftechnik / Kunststofftechnik	ger
dcterms.source.volume	Band 16
kup.iskup	true
kup.price	39,00
kup.series	Schriftenreihe des Instituts für Werkstofftechnik / Kunststofftechnik
kup.subject	Naturwissenschaft, Technik, Informatik, Medizin
kup.typ	Dissertation
kup.institution	FB 15 / Maschinenbau
kup.binding	Softcover
kup.size	DIN A5
ubks.epflicht	true