Suche
Anzeige der Dokumente 1-10 von 21
Aufsatz
On the reliability of residual stress measurements in unidirectional carbon fibre reinforced epoxy composites
(2021-03-03)
The present work introduces a novel methodology to analyse non-uniform residual stresses in composite materials. For robust determination of stresses in complex structures made of different layers, it is first necessary to prove that residual stress analysis in a single layer structure can reliably be accomplished. In present work a unidirectional carbon fibre reinforced epoxy is investigated. For residual stress determination, the integral incremental hole drilling method is used. It is revealed that the standard ...
Aufsatz
Consequences of Deep Rolling at Elevated Temperature on Near-Surface and Fatigue Properties of High-Manganese TWIP Steel X40MnCrAl19-2
(2021-11-05)
Due to pronounced work-hardening induced by the complex interplay of deformation mechanisms such as dislocation slip, twinning and/or martensitic phase transformation, high-manganese steels represent a class of materials well-suited for mechanical surface treatment. In the present study, the fatigue behavior of a high-mangsanese steel showing twinning-induced plasticity (TWIP) effect at room temperature (RT) was investigated after deep rolling at 550 °C. Results are compared to a former study discussing the behavior ...
Aufsatz
On the low-cycle fatigue behavior of thermo-mechanically processed high-strength aluminum alloys
(2021)
In the present work low-cycle fatigue experiments were carried out on thermo-mechanically processed AA6082 and AA7075 sheets to evaluate mechanical properties under cyclic loading. Different cooling rates imposed by use of tempered forming tools after solutionizing and subsequent aging treatment led to the formation of precipitates with differing sizes and morphologies. Specimens thermo-mechanically processed in tools with temperatures of 24 °C and 200 °C showed superior mechanical properties under both monotonic and ...
Dissertation
Bewertung von Eigenspannungen nach dem Laserstrahlhärten von komplex geformten Komponenten und additiv gefertigten Bauteilen
(2021)
Die Laserstrahlbearbeitung hat sich im Laufe der letzten Jahre zu einem wichtigen Forschungsschwerpunkt in industrieller und akademischer Hinsicht entwickelt. Neben der Erschließung neuer Anwendungsgebiete durch den Vorteil einer hohen Bearbeitungsflexibilität überzeugt die laserbasierte Materialbearbeitung vor allem durch einen lokal beeinflussbaren Energieeintrag. Jedoch sind derzeit mit zunehmender geometrischer Komplexität und Bauteilgröße nur begrenzte Tiefenwirkungen der gewünschten Druckeigenspannungen ...
Aufsatz
Effect of Crystallographic Orientation and Grain Boundaries on Martensitic Transformation and Superelastic Response of Oligocrystalline Fe–Mn–Al–Ni Shape Memory Alloys
(2021-07-26)
In situ tensile tests employing digital image correlation were conducted to study the martensitic transformation of oligocrystalline Fe–Mn–Al–Ni shape memory alloys in depth. The influence of different grain orientations, i.e., near-〈001〉 and near-〈101〉, as well as the influence of different grain boundary misorientations are in focus of the present work. The results reveal that the reversibility of the martensite strongly depends on the type of martensitic evolving, i.e., twinned or detwinned. Furthermore, it is ...
Aufsatz
Shape Memory Effect and Superelasticity of [001]-Oriented FeNiCoAlNb Single Crystals Aged under and without Stress
(2021-06-10)
The two-step ageing of Fe-28Ni-17Co-11.5Al-2.5Nb (at.%) single crystals under and without stress, leads to the precipitation of the γ′- and β-phase particles. Research has shown that γ–α′ thermoelastic martensitic transformation (MT), with shape memory effect (SME) and superelasticity (SE), develops in the [001]-oriented crystals under tension. SE was observed within the range from the temperature of the start of MT upon cooling Mₛ, to the temperature of the end of the reverse MT upon heating Af, and at temperatures ...
Aufsatz
The Effect of Fiber Waviness on the Residual Stress State and Its Prediction by the Hole Drilling Method in Fiber Metal Laminates: A Global-Local Finite Element Analysis
(2021-01-15)
In this paper, fiber waviness, as one of the most frequently occurring defects in fiber reinforced composites, is numerically investigated with regard to the formation of residual stresses in fiber metal laminates. Furthermore, the prediction of the residual stress state in the thickness direction by means of the simulated hole drilling method is studied. To this regard, a global-local finite element analysis based on the submodel technique is presented. The submodel technique essentially consists of two governing ...
Aufsatz
Cyclic Crack Growth in Chemically Tailored Isotropic Austenitic Steel Processed by Electron Beam Powder Bed Fusion
(2021-11-01)
The present study analyzes the cyclic crack propagation behavior in an austenitic steel processed by electron beam powder bed fusion (PBF-EB). The threshold value of crack growth as well as the crack growth behavior in the Paris regime were studied. In contrast to other austenitic steels, the building direction during PBF-EB did not affect the crack propagation rate, i.e., the crack growth rates perpendicular and parallel to the building direction were similar due to the isotropic microstructure characterized by ...
Aufsatz
Tribological Performance of Additively Manufactured AISI H13 Steel in Different Surface Conditions
(2021-02-16)
Additive manufacturing of metallic tribological components offers unprecedented degrees of freedom, but the surface roughness of most as-printed surfaces impedes the direct applicability of such structures, and postprocessing is necessary. Here, the tribological performance of AISI H13 steel samples was studied. These were additively manufactured through laser powder bed fusion (L-PBF), also referred to as selective laser melting (SLM). Samples were tested in four different surface conditions: as-printed, polished, ...
Aufsatz
Overmoulding of Additively Manufactured Titanium Inserts Using Polyoxymethylene (POM)—Evaluation of Bond Quality as a Function of Process Parameters
(2021-06-15)
Due to their process-induced porous surfaces, additively manufactured structures are not optimized for applications in which friction is a key factor. To improve the frictional properties of additively manufactured titanium inserts of various thicknesses, two tribologically optimized POM materials, which differ in terms of filler composition and contents, were used to overmould the inserts. The titanium inserts were manufactured in two different building directions, resulting in a variation in surface roughness. The ...