On the Influence of Microstructure on the Corrosion Behavior of Fe–Mn–Al–Ni Shape Memory Alloy in 5.0 wt% NaCl Solution
(2020-10-03)
Herein the corrosion behavior of Fe–Mn–Al–Ni shape memory alloys characterized by different microstructures in a 5.0 wt% NaCl solution is investigated. Open circuit potential and potentiodynamic polarisation tests are conducted. Generally, Fe–Mn–Al–Ni shows corrosion properties being similar to pure iron. However, the polarization curves of single crystals indicate the presence of an unstable passive system. The corrosion damage is analyzed by means of optical microscopy and electron microscopy. It is revealed that ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Thermal Stability of Residual Stresses in Differently Deep Rolled Surface Layers of Steel SAE 1045
(2021-05-07)
The stability of compressive residual stresses generated by deep rolling plays a decisive role on the fatigue behavior of specimens and components, respectively. In this regard, deep rolling at elevated temperature has proven to be very effective in stabilizing residual stresses when fatigue analysis is conducted at ambient temperature. However, since residual stresses can be affected not only by plastic deformation but also when thermal energy is provided, it is necessary to analyze the influence of temperature and ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
On the low-cycle fatigue behavior of thermo-mechanically processed high-strength aluminum alloys
(2021)
In the present work low-cycle fatigue experiments were carried out on thermo-mechanically processed AA6082 and AA7075 sheets to evaluate mechanical properties under cyclic loading. Different cooling rates imposed by use of tempered forming tools after solutionizing and subsequent aging treatment led to the formation of precipitates with differing sizes and morphologies. Specimens thermo-mechanically processed in tools with temperatures of 24 °C and 200 °C showed superior mechanical properties under both monotonic and ...