Aufsatz
Micromechanical Modeling of AlSi10Mg Processed by Laser-Based Additive Manufacturing: From as-Built to Heat-Treated Microstructures
(2022-08-13)
The unique microstructure of the alloy AlSi10Mg produced by the laser-based powder bed fusion of metals (PBF-LB/M) provides high-strength and high-strain-hardening capabilities of the material. The microstructure and mechanical properties of 3D-printed, i.e., additively manufactured, AlSi10Mg are significantly altered by post-building heat-treatment processes applied in order to tailor the final properties of the parts. Using an accurate computational model to predict and improve the mechanical performance of 3D-printed ...
Aufsatz
Investigation of processing windows in additive manufacturing of AlSi10Mg for faster production utilizing data-driven modeling
(2022-04-29)
To reduce production time and decrease production cost, the increase of layer thickness is an adequate option in powder bed fusion. In order to determine the relationships between process parameters in laser powder bed fusion (PBF-LB/M) and final porosity in AlSi10Mg, samples were processed following a space-filling experimental design in the present study. A total of 144 samples were fabricated considering layer thicknesses of 30 µm, 45 µm, 60 µm, and 90 µm. Afterwards, porosity was assessed using image analysis and ...
Aufsatz
Oxide Modified Iron in Electron Beam Powder Bed Fusion - From Processability to Corrosion Properties
(2022-03-07)
Additive manufacturing (AM) processes are not solely used where maximum design freedom meets low lot sizes. Direct microstructure design and topology optimization can be realized concomitantly during processing by adjusting the geometry, the material composition, and the solidification behavior of the material considered. However, when complex specific requirements have to be met, a targeted part design is highly challenging. In the field of biodegradable implant surgery, a cytocompatible material of an application-adapted ...
Aufsatz
Cooling rate as a process parameter in advanced roll forming to tailor microstructure,mechanical and corrosion properties of EN AW 7075 tubes
(2022-12-14)
The effects of solution heat treatment parameters and quench media as a processing tool for tailoring microstructure, mechanical and corrosion properties in roll forming of EN AW 7075 alloy were studied. The highest yield stress and ultimate tensile strength were obtained for the specimens quenched in water, while the air-cooled specimens exhibited inferior mechanical properties. Microstructural analysis of specimens showed that except water-quenched specimens, the parts cooled/quenched in oil, in direct contact with ...