Aufsatz
Comparative investigation of two-dimensional imaging methods and X-ray tomography in the characterization of microstructure
(2017-10-02)
The microstructural features of three different materials have been quantified by means of 2D image analysis and X-ray micro-computer tomography (CT) and the results were compared to determine the reliability of the 2D analysis in the material characterization. The 3D quantification of shrinkage pores and Fe-rich inclusions of an Al-Si-Cu alloy by X-ray tomography was compared with the statistical analysis of the 2D metallographic pictures and a significant difference in the results was found due to the complex ...
Aufsatz
Investigations on Tightness of Polymer-Metal Hybrids in Environments with Thermal, Media, and Mechanical Loads
(2017-07-31)
With polymer-metal hybrids becoming more commonly used as structural components it was investigated how they perform in complex environments with combined thermal, media, and mechanical loads. Special attention was put on media tightness under said loads. This paper sums up the activities of the polymer technology research group of the University of Kassel on hybrids produced by overmolding metal inserts. Investigations concerning joint strength and influence of (cyclic) temperature loads and chemical corrosion on ...
Aufsatz
Mechanical Properties of Polydimethylsiloxane as a Function of the Amount and Type of Crosslinking Agent
(2017-06-13)
In this investigation, a high-consistency rubber (HCR) was mixed with five different, typically used crosslinking agents that are based on organic peroxide. Furthermore, the amount of crosslinking agent was varied in order to quantify the effect on the mechanical properties. All materials were processed in a hot pressing process, and, subsequently, post-cured. The properties were characterized by the measurement of the swelling ratio, shore A-hardness, rebound resilience and tensile test. We successfully proved that ...