The Effect of Injection Molding Parameters on Microcellular Foam Morphology
(2021)
Microcellular foam injection molding with physical blowing agent (MuCell®) delivers monetary benefits, processing advantages and freedom of product design by reducing shrinkage. In conjunction with an advanced mold technology, so-called Pull and Foam method, there is great potential in controlling the foam structure of the component locally. In this study, Polycarbonate (PC) components were produced with nearly compact outer skin and a closed cellular core. To understand the relation between processing parameters and ...
Konferenzveröffentlichung
Effects of the Cellular Morphology on Fatigue Deformation Mechanisms of Physically Foamed Polycarbonate
(2023)
In this study, the tension–tension fatigue behavior of foam injection molded thermoplastic microcellular Polycarbonate (PC) is characterized. The variation in morphology is obtained by modifying the mold temperature, injection volume, injection flow rate, and blowing agent content (physical and chemical) in the polymer melt. The relationship between the wide range of morphological qualities and relevant fatigue properties is made explicit via a statistical correlation coefficient analyses. The analysis is made between ...
Aufsatz
Parameter recommendation for injection molding based on similarity analysis of injection molded parts
(2023)
Injection molding is a widespread manufacturing process for producing complex plastic shapes. The process is controlled by a large number of parameters, which show interactions with each other. Thereby the determination of an optimal operating point during sampling is a resource-consuming and demanding task. The data, which is generated during sampling, is usually not used for subsequent sampling processes. In the context of Industry 4.0, manufacturing companies attempt to optimize production efficiency to save time ...
Aufsatz
Effects of blending poly(lactic acid) and thermoplastic polyester polyurethanes on the mechanical and adhesive properties in two-component injection molding
(2022-09-16)
One possible way to increase the use of bioplastics and thus contribute to a more resource-efficient and sustainable economy is to broaden the application range of such bioplastics. Poly(lactic acid) (PLA) is a promising and commercially available bio-based and biologically degradable polymer, which exhibits a high strength and stiffness but is very brittle. Blending with other polymers can lead to an enhancement of the ductility of the PLA. The goal of this work was to show that blending of PLA with a bio-based ...
Aufsatz
Influence of ethylene oxide and gamma irradiation sterilization processes on the degradation behaviour of poly(lactic acid) (PLA) in the course of artificially accelerated aging
(2024-02-10)
To promote the application of bio-based materials in the field of medical technology, it is essential to conduct additional research, focusing on their long-term performance after sterilization. For this purpose, the study examines the aging behaviour of three poly(lactic-acid) (PLA) materials, sterilized with either ethylene oxide or gamma irradiation, over a two years aging period, in accordance with ASTM F1980-21. During these investigations, a direct correlation between moisture absorption and degradation progression ...
Aufsatz
Modification of self-reinforced composites (SRCs) via film stacking process
(2022-02-25)
This work presents the mechanical behavior of self-reinforced composites (SRCs) manufactured and modified via film stacking. For modification, interleaved films made of polypropylene (PP), a thermoplastic elastomer and a polyolefin engage were combined in different ways to induce the elastic modifier into the matrix material. The content of modifier was also varied in two ways. First, the films were produced out of a single material and second out of a compound. So, the same content of modifier was implemented in two ...
Aufsatz
Investigation of the adhesive strength in a combined compaction and back-injection process to produce back-injected self-reinforced composites (SRCs)
(2022-03-08)
This publication investigates the adhesion between an injection molded component and a self-reinforced composite (SRC) produced in a combined compaction and back-injection process to produce back-injected self-reinforced composites. To study the influence of the process, the parameters barrel temperature, time of injection, and tool temperature were varied. In addition, samples were taken at different positions along the flow path. In light of the orthotropic material behavior of SRCs, investigations were conducted ...
Aufsatz
Holzdesign trifft Kunststofftechnik
(2022)
Werkstoffverbunde aus Holzgeweben in einer thermoplastischen Matrix verbinden die Idee des textilen Holzbaus mit der Faserverbundtechnologie. In einem Projekt werden Fassadenelemente aus solchen Wood Textile Composites hergestellt. Dabei spielt neben den mechanischen Anforderungen auch die gestalterische Seite und die Akzeptanz der zukünftigen Nutzer eine wichtige Rolle.
Aufsatz
Influences on the mechanical properties of SRCs in a combined compacting and back injecting process
(2022-03-03)
In this research paper, the effects of the combined compacting and back-injection process to produce back-injected self-reinforced composites on the mechanical properties of the self-reinforced composites (SRCs) are investigated. For this purpose, the parameters barrel temperature, time of injection and holding pressure were varied for the back injection. Tensile and bending tests were carried out on the SRCs. The results show that the mechanical properties depend to a large extent on the process parameters. The ...
Aufsatz
Simultaneous impact modified and chain extended glass fiber reinforced poly(lactic acid) composites: Mechanical, thermal, crystallization, and dynamic mechanical performance
(2021-02-05)
Herein, glass fiber (GF) reinforced binary, ternary, and quaternary poly(lactic acid) (PLA) composites were prepared. Toughening, and chain extension of PLA was achieved through the incorporation of impact modifier and chain extender and their concurrent effects on the spectroscopic, crystallization, mechanical, thermal, and thermomechanical properties of the composites were investigated. High mechanical properties of GF influenced the mechanical performance of the composites. However, GF alone could not restrict the ...