Aufsatz
Microstructural Constituents and Mechanical Properties of Low-Density Fe-Cr-Ni-Mn-Al-C Stainless Steels
(2022-07-23)
Metallic material concepts associated with the sustainable and efficient use of resources are currently the subject of intensive research. Al addition to steel offers advantages in view of lightweight, durability, and efficient use of high-Fe scrap from the Al industry. In the present work, Al was added to Fe-12Cr-(9,12)Ni-3Mn-0.3C-xAl (x = 0.1–6) (wt.%) stainless steels to assess its influence on microstructure and mechanical properties. According to density measurements based on Archimedes’ principle, densities ...
Aufsatz
Microcantilever Fracture Tests of α-Cr Containing NiAl Bond Coats
(2022-01-08)
MCrAlY bond coats are widely used as oxidation-resistant coatings on superalloys. The major phase is the thermally stable intermetallic β-NiAl phase. The addition of Cr increases the oxidation and corrosion resistance but leads to the formation of α-Cr precipitates. Both phases are brittle and limit the fracture toughness of these coatings. To study the influence of thermal exposure and the resulting changing chemical composition on the fracture properties, the fracture toughness of both phases is measured by notched ...
Aufsatz
Determination and Validation of Residual Stresses in CFRP/Metal Hybrid Components Using the Incremental Hole Drilling Method
(2020-09-21)
Lightweight materials contribute to an efficient decrease in fuel consumption in the automotive and aircraft industries. Hybrid components made of metal and carbon fiber-reinforced plastics (CFRP) have a high potential in lightweight applications due to their high strength-to-weight ratio. For cost-effective processing of hybrid materials, advanced manufacturing processes such as the prepreg-press-technology have been developed, in which the bonding between a metallic component and a fiber compound is exclusively ...
Konferenzveröffentlichung
Microstructural and Mechanical Properties of AISI 4140 Steel Processed by Electron Beam Powder Bed Fusion Analyzed Using Miniature Samples
(ASTM International, 2022-02-26)
The present study reports on the identification of an adequate process window for electron beam powder bed fusion (E-PBF) of AISI 4140 steel. For characterization, only miniature samples were used. It is clearly revealed that, for comparison and evaluation of different conditions, the use of such small samples is absolutely sufficient, even under fatigue loading. The initial E-PBF as-built condition is compared with conventionally heat-treated conditions (i.e., normalized as well as quenched and tempered). Based on ...
Aufsatz
Investigation of processing windows in additive manufacturing of AlSi10Mg for faster production utilizing data-driven modeling
(2022-04-29)
To reduce production time and decrease production cost, the increase of layer thickness is an adequate option in powder bed fusion. In order to determine the relationships between process parameters in laser powder bed fusion (PBF-LB/M) and final porosity in AlSi10Mg, samples were processed following a space-filling experimental design in the present study. A total of 144 samples were fabricated considering layer thicknesses of 30 µm, 45 µm, 60 µm, and 90 µm. Afterwards, porosity was assessed using image analysis and ...
Aufsatz
Influence of Surface Mechanical Attrition Treatment (SMAT) on Microstructure, Tensile and Low-Cycle Fatigue Behavior of Additively Manufactured Stainless Steel 316L
(2023-08-29)
Direct Energy Deposition (DED), as one common type of additive manufacturing, is capable of fabricating metallic components close to net-shape with complex geometry. Surface mechanical attrition treatment (SMAT) is an advanced surface treatment technology which is able to yield a nanostructured surface layer characterized by compressive residual stresses and work hardening, thereby improving the fatigue performances of metallic specimens. In the present study, stainless steel 316L specimens were fabricated by DED and ...
Aufsatz
A comparative study using water atomized and gas atomized powder in laser powder bed fusion process – Assessment of the fatigue performance
(2022)
Gas-atomized (GA, spherical) and water-atomized (WA, spattered) commercially pure iron (cp-Fe) powders were processed using laser-based powder bed fusion, resulting in a slightly higher porosity of the WA condition. In addition to characterization of quasi-static mechanical properties, fatigue tests, which are known to be detrimentally affected by porosity, were finally considered, revealing good properties even for the WA condition. In terms of microstructure stability, the GA and WA specimens significantly differ; ...
Aufsatz
On the influence of ϰ-carbides on the low-cycle fatigue behavior of high-Mn light-weight steels
(2021)
High-manganese light-weight steels offer a great potential for structural purposes in the mobility sector due to their reduced density combined with outstanding mechanical properties. As many of the envisaged applications of these materials will suffer from cyclic loading during their service life, the fundamentals of their fatigue behavior must be studied extensively. In the present work, the low-cycle fatigue (LCF) properties of an austenitic Fe-29.8Mn-7.65Al-1.11C light-weight steel were investigated. Two ...
Aufsatz
On the structural integrity of Fe-36Ni Invar alloy processed by selective laser melting
(2020)
Specimens made from pre-alloyed Invar (Fe-36Ni) powder were fabricated by selective laser melting and stress-relief heat treated afterwards. A relative density of the fabricated parts of 99.6 % was determined by computed tomography. The microstructure and mechanical behavior under monotonic and particularly cyclic loading at ambient temperature were investigated. Results reveal a bimodal microstructure containing columnar and equiaxed grains with an average grain size of 75 μm and pronounced texture 〈001〉 || BD. The ...
Aufsatz
Pathways toward the Use of Non-Destructive Micromagnetic Analysis for Porosity Assessment and Process Parameter Optimization in Additive Manufacturing of 42CrMo4 (AISI 4140)
(2024-02-20)
Laser-based powder bed fusion of metals (PBF-LB/M) is a widely applied additive manufacturing technique. Thus, PBF-LB/M represents a potential candidate for the processing of quenched and tempered (Q&T) steels such as 42CrMo4 (AISI 4140), as these steels are often considered as the material of choice for complex components, e.g., in the toolmaking industry. However, due to the presence of process-induced defects, achieving a high quality of the resulting parts remains challenging in PBF-LB/M. Therefore, an extensive ...