Aufsatz
Influence of ethylene oxide and gamma irradiation sterilization processes on the degradation behaviour of poly(lactic acid) (PLA) in the course of artificially accelerated aging
(2024-02-10)
To promote the application of bio-based materials in the field of medical technology, it is essential to conduct additional research, focusing on their long-term performance after sterilization. For this purpose, the study examines the aging behaviour of three poly(lactic-acid) (PLA) materials, sterilized with either ethylene oxide or gamma irradiation, over a two years aging period, in accordance with ASTM F1980-21. During these investigations, a direct correlation between moisture absorption and degradation progression ...
Aufsatz
Mechanical Characterization and Simulation of Wood Textile Composites (WTC) supported by Digital Image Correlation (DIC)
(2023-05-30)
Wood Textile Composites (WTC) based on willow wood fabrics and polypropylene were produced using a hot compacting process in order to open up new and innovative areas of applications for wood. Due to their attractive and variable design, the WTCs are to be used in areas with a high visual impact, for example as a facade element. In tensile and 3-point bending tests, it was shown that the mechanical properties of WTC are strongly dependent on the heterogeneous structure of the composite. Both strength and elongation ...
Aufsatz
Energy Resolved Residual Stress Analysis with Laboratory X-Ray Sources
(2017-04-17)
It is well known that existing residual stress fields play an important role for strength and lifetime of components. Consequently there is a great interest in the availability of fast, reliable and possibly nondestructive methods for their determination. In this context, X-ray diffraction methods play an important role in technical practice as well as in scientific research. They are based on the determination of lattice strains from which residual stresses are determined applying Hooke's law with appropriate elastic ...
Dissertation
Optimierung des Risikomanagements als Beitrag zur Steigerung des Projekterfolgs bei Produktentwicklungsprojekten am Beispiel der Automobilindustrie
(2024)
Die zunehmende Projektifizierung der letzten Jahrzehnte hat dazu geführt, dass der Beitrag von Projekten zur Erreichung der Unternehmensziele und damit zur unternehmerischen Wert-schöpfung in gleichem Maße gestiegen ist. Gleichzeitig sind Projekte aufgrund ihres einzigar-tigen Charakters mit Risiken und Unsicherheiten behaftet, deren Auftreten im Kontext der Produktentwicklung in der Automobilindustrie durch den Produktivitätsdruck sowie die stetig steigende Komplexität und Dynamik noch verstärkt wird. Die negativen ...
Aufsatz
Prozessintegration von induktiver Wärmebehandlung und Festwalzen – sichere und zuverlässige Komponenten mit hoher Schwingfestigkeit
(2017-02-08)
Mechanische Oberflächenbehandlungen, beispielsweise das Festwalzen, spielen in der technischen Praxis eine bedeutende Rolle und tragen wesentlich zur Steigerung der Zuverlässigkeit hochbeanspruchter Komponenten bei. In einer Reihe von Fällen wurde gezeigt, dass eine Erhöhung der Prozesstemperatur die Wirksamkeit der Verfahren noch steigert, weil dies zu einer besseren Stabilisierung der eingebrachten Druckeigenspannungen führt. Eine wesentliche Voraussetzung zur Einführung dieser Verfahren in die Praxis ist allerdings, ...
Aufsatz
High Consistency Silicone Rubber Foams
(2024-04-23)
Silicone elastomers are high-performance plastics. In the extrusion process, only high-consistency silicone rubbers were used. In order to reduce the cost and weight, silicone rubbers can be foamed during processing. In this study, high-consistency silicone rubber is processed with different physical and chemical blowing agents. The resulting reaction kinetics, as well as the mechanical and morphological properties, had been investigated and compared with each other. This showed that the chemical blowing agent ...
Aufsatz
Pathways toward the Use of Non-Destructive Micromagnetic Analysis for Porosity Assessment and Process Parameter Optimization in Additive Manufacturing of 42CrMo4 (AISI 4140)
(2024-02-20)
Laser-based powder bed fusion of metals (PBF-LB/M) is a widely applied additive manufacturing technique. Thus, PBF-LB/M represents a potential candidate for the processing of quenched and tempered (Q&T) steels such as 42CrMo4 (AISI 4140), as these steels are often considered as the material of choice for complex components, e.g., in the toolmaking industry. However, due to the presence of process-induced defects, achieving a high quality of the resulting parts remains challenging in PBF-LB/M. Therefore, an extensive ...
Aufsatz
Modification of self-reinforced composites (SRCs) via film stacking process
(2022-02-25)
This work presents the mechanical behavior of self-reinforced composites (SRCs) manufactured and modified via film stacking. For modification, interleaved films made of polypropylene (PP), a thermoplastic elastomer and a polyolefin engage were combined in different ways to induce the elastic modifier into the matrix material. The content of modifier was also varied in two ways. First, the films were produced out of a single material and second out of a compound. So, the same content of modifier was implemented in two ...
Aufsatz
Bend Straightening of a Carbonitrided Gear Shaft – Consequences on Residual Stresses and Retained Austenite near the Surface
(2017-06-20)
Carbonitriding of shafts in drive technology is strongly connected with distortion. Bend straightening is an important process step in order to eliminate distortion without removing the hardened surface layer. As shown in several investigations, even for simple part geometries, bending induced stresses and plastic deformations have a strong impact not only on the residual stress state but also on the microstructure after straightening. As gear shafts become increasingly filigree and complex in their geometry, the ...
Aufsatz
Investigation of the adhesive strength in a combined compaction and back-injection process to produce back-injected self-reinforced composites (SRCs)
(2022-03-08)
This publication investigates the adhesion between an injection molded component and a self-reinforced composite (SRC) produced in a combined compaction and back-injection process to produce back-injected self-reinforced composites. To study the influence of the process, the parameters barrel temperature, time of injection, and tool temperature were varied. In addition, samples were taken at different positions along the flow path. In light of the orthotropic material behavior of SRCs, investigations were conducted ...