Aufsatz
A new method for microscale cyclic crack growth characterization from notched microcantilevers and application to single crystalline tungsten and a metallic glass
(2022-06-22)
The lifetime of most metals is limited by cyclic loads, ending in fatigue failure. The progressive growth of cracks ends up in catastrophic failure. An advanced method is presented for the determination of cyclic crack growth on the microscale using a nanoindenter, which allows the characterization of > 10,000 loading cycles. It uses focused ion beam fabricated notched microcantilevers. The method has been validated by cyclic bending metallic glass and tungsten microcantilevers. The experiments reveal a stable crack ...
Aufsatz
Mechanics of colloidal supraparticles under compression
(2021-10-13)
Colloidal supraparticles are finite, spherical assemblies of many primary particles. To take advantage of their emergent functionalities, such supraparticles must retain their structural integrity. Here, we investigate their size-dependent mechanical properties via nanoindentation. We find that the deformation resistance inversely scales with the primary particle diameter, while the work of deformation is dependent on the supraparticle diameter. We adopt the Griffith theory to such particulate systems to provide a ...
Aufsatz
Describing mechanical damage evolution through in situ electrical resistance measurements
(2023-02-27)
The fatigue properties of metallizations used as electrical conductors in flexible electronic devices have been thoroughly studied over the years. Most studies use time-intensive characterization methods to evaluate mechanical damage. For their ease of access, in situ electrical resistance measurements are often performed along with other characterization methods. However, the data are mostly used as an indicator of failure and a thorough analysis is usually missing. This work presents some deeper analysis methods ...
Aufsatz
Linking through-thickness cracks in metallic thin films to in-situ electrical resistance peak broadening
(2022-01-29)
Measurements of electrical resistance have been used extensively as a failure criterion in cyclically loaded conductive films. However, not much research has been performed on extracting additional information contained within such resistance data sets. This study shows that an increase in peak width evidences a transition from cracks bridging to through-thickness crack formation. A Au/Cr bilayer system on a polyimide substrate is used for data generation but the method is applicable to any material system where both ...