A new method for microscale cyclic crack growth characterization from notched microcantilevers and application to single crystalline tungsten and a metallic glass
(2022-06-22)
The lifetime of most metals is limited by cyclic loads, ending in fatigue failure. The progressive growth of cracks ends up in catastrophic failure. An advanced method is presented for the determination of cyclic crack growth on the microscale using a nanoindenter, which allows the characterization of > 10,000 loading cycles. It uses focused ion beam fabricated notched microcantilevers. The method has been validated by cyclic bending metallic glass and tungsten microcantilevers. The experiments reveal a stable crack ...
Aufsatz
Linking through-thickness cracks in metallic thin films to in-situ electrical resistance peak broadening
(2022-01-29)
Measurements of electrical resistance have been used extensively as a failure criterion in cyclically loaded conductive films. However, not much research has been performed on extracting additional information contained within such resistance data sets. This study shows that an increase in peak width evidences a transition from cracks bridging to through-thickness crack formation. A Au/Cr bilayer system on a polyimide substrate is used for data generation but the method is applicable to any material system where both ...