Microcantilever Fracture Tests of α-Cr Containing NiAl Bond Coats
(2022-01-08)
MCrAlY bond coats are widely used as oxidation-resistant coatings on superalloys. The major phase is the thermally stable intermetallic β-NiAl phase. The addition of Cr increases the oxidation and corrosion resistance but leads to the formation of α-Cr precipitates. Both phases are brittle and limit the fracture toughness of these coatings. To study the influence of thermal exposure and the resulting changing chemical composition on the fracture properties, the fracture toughness of both phases is measured by notched ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Investigation of processing windows in additive manufacturing of AlSi10Mg for faster production utilizing data-driven modeling
(2022-04-29)
To reduce production time and decrease production cost, the increase of layer thickness is an adequate option in powder bed fusion. In order to determine the relationships between process parameters in laser powder bed fusion (PBF-LB/M) and final porosity in AlSi10Mg, samples were processed following a space-filling experimental design in the present study. A total of 144 samples were fabricated considering layer thicknesses of 30 µm, 45 µm, 60 µm, and 90 µm. Afterwards, porosity was assessed using image analysis and ...
Aufsatz
![Eingeschränkter Zugang](/themes/Mirage2/images/lock-128.png)
A comparative study using water atomized and gas atomized powder in laser powder bed fusion process – Assessment of the fatigue performance
(2022)
Gas-atomized (GA, spherical) and water-atomized (WA, spattered) commercially pure iron (cp-Fe) powders were processed using laser-based powder bed fusion, resulting in a slightly higher porosity of the WA condition. In addition to characterization of quasi-static mechanical properties, fatigue tests, which are known to be detrimentally affected by porosity, were finally considered, revealing good properties even for the WA condition. In terms of microstructure stability, the GA and WA specimens significantly differ; ...