Suche
Anzeige der Dokumente 31-40 von 72
Aufsatz
Joining of Contact Pins and Conductive Compounds via Injection Molding – Influence of the Flow Situation on the Electrical Contact Resistance
(2020-04-09)
While a lot of research can be found in the field of bulk resistance of carbon filled polymers, comparatively few papers focus on contact resistance between compound and metal contacts. Due to that small number of researches that deal with contact resistances, studies of the influence of injection molding conditions and parameters on the contact resistance are also very rare. In contradiction to that, these influences on bulk resistance have been studied. The objective of this work was to investigate the electrical ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Effects of aging on the stress-induced martensitic transformation and cyclic superelastic properties in Co-Ni-Ga shape memory alloy single crystals under compression
(2022)
Co-Ni-Ga shape memory alloys attracted scientific attention as promising candidate materials for damping applications at elevated temperatures, owing to excellent superelastic properties featuring a fully reversible stress-strain response up to temperatures as high as 500 °C. In the present work, the effect of aging treatments conducted in a wide range of aging temperatures and times, i.e. at 300–400 °C for 0.25–8.5 h, was investigated. It is shown that critical features of the martensitic transformation are strongly ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Effect of Crystallographic Orientation and Grain Boundaries on Martensitic Transformation and Superelastic Response of Oligocrystalline Fe–Mn–Al–Ni Shape Memory Alloys
(2021-07-26)
In situ tensile tests employing digital image correlation were conducted to study the martensitic transformation of oligocrystalline Fe–Mn–Al–Ni shape memory alloys in depth. The influence of different grain orientations, i.e., near-〈001〉 and near-〈101〉, as well as the influence of different grain boundary misorientations are in focus of the present work. The results reveal that the reversibility of the martensite strongly depends on the type of martensitic evolving, i.e., twinned or detwinned. Furthermore, it is ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Shape Memory Effect and Superelasticity of [001]-Oriented FeNiCoAlNb Single Crystals Aged under and without Stress
(2021-06-10)
The two-step ageing of Fe-28Ni-17Co-11.5Al-2.5Nb (at.%) single crystals under and without stress, leads to the precipitation of the γ′- and β-phase particles. Research has shown that γ–α′ thermoelastic martensitic transformation (MT), with shape memory effect (SME) and superelasticity (SE), develops in the [001]-oriented crystals under tension. SE was observed within the range from the temperature of the start of MT upon cooling Mₛ, to the temperature of the end of the reverse MT upon heating Af, and at temperatures ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Micromechanical Modeling of AlSi10Mg Processed by Laser-Based Additive Manufacturing: From as-Built to Heat-Treated Microstructures
(2022-08-13)
The unique microstructure of the alloy AlSi10Mg produced by the laser-based powder bed fusion of metals (PBF-LB/M) provides high-strength and high-strain-hardening capabilities of the material. The microstructure and mechanical properties of 3D-printed, i.e., additively manufactured, AlSi10Mg are significantly altered by post-building heat-treatment processes applied in order to tailor the final properties of the parts. Using an accurate computational model to predict and improve the mechanical performance of 3D-printed ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Influence of the Miniaturisation Effect on the Effective Stiffness of Lattice Structures in Additive Manufacturing
(2020-10-29)
Thin-walled and cellular structures are characterised by superior lightweight potential due to their advantageous stiffness to weight ratio. They find particular interest in the field of additive manufacturing due to robust and reproducible manufacturability. However, the mechanical performance of such structures strongly depends on the manufacturing process and resultant geometrical imperfections such as porosity, deviations in strut thickness or surface roughness, for which an understanding of their influence is ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
The Effect of Fiber Waviness on the Residual Stress State and Its Prediction by the Hole Drilling Method in Fiber Metal Laminates: A Global-Local Finite Element Analysis
(2021-01-15)
In this paper, fiber waviness, as one of the most frequently occurring defects in fiber reinforced composites, is numerically investigated with regard to the formation of residual stresses in fiber metal laminates. Furthermore, the prediction of the residual stress state in the thickness direction by means of the simulated hole drilling method is studied. To this regard, a global-local finite element analysis based on the submodel technique is presented. The submodel technique essentially consists of two governing ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Cyclic Crack Growth in Chemically Tailored Isotropic Austenitic Steel Processed by Electron Beam Powder Bed Fusion
(2021-11-01)
The present study analyzes the cyclic crack propagation behavior in an austenitic steel processed by electron beam powder bed fusion (PBF-EB). The threshold value of crack growth as well as the crack growth behavior in the Paris regime were studied. In contrast to other austenitic steels, the building direction during PBF-EB did not affect the crack propagation rate, i.e., the crack growth rates perpendicular and parallel to the building direction were similar due to the isotropic microstructure characterized by ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Linking through-thickness cracks in metallic thin films to in-situ electrical resistance peak broadening
(2022-01-29)
Measurements of electrical resistance have been used extensively as a failure criterion in cyclically loaded conductive films. However, not much research has been performed on extracting additional information contained within such resistance data sets. This study shows that an increase in peak width evidences a transition from cracks bridging to through-thickness crack formation. A Au/Cr bilayer system on a polyimide substrate is used for data generation but the method is applicable to any material system where both ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Additive Manufacturing of 3D Luminescent ZrO2:Eu3+ Architectures
(2022-04-27)
Implementation of more refined structures at the nano to microscale is expected to advance applications in optics and photonics. This work presents the additive manufacturing of 3D luminescent microarchitectures emitting light in the visible range. A tailor-made organo-metallic resin suitable for two-photon lithography is developed, which upon thermal treatment in an oxygen-rich atmosphere allows the creation of silicon-free tetragonal (t-) and monoclinic (m-) ZrO₂. The approach is unique because the tailor-made ...