Aufsatz
Ti6Al4V lattice structures manufactured by electron beam powder bed fusion - Microstructural and mechanical characterization based on advanced in situ techniques
(2022-12-17)
Powder bed fusion (PBF) processes enable the manufacturing of complex components in a time- and cost-efficient manner. Especially lattice structures are currently focused since they show varying mechanical properties, including different deformation and damage behaviors, which can be used to locally tailor the mechanical behavior. However, the present process-structure-property relationships are highly complex and have to be understood in detail in order to enable an implementation of PBF manufactured lattice structures ...
Dissertation
Untersuchung von Gussporen in einer Aluminium-Gusslegierung mit der Computertomographie
(2022-04)
In dieser Arbeit wird das Schädigungsverhalten einer Aluminium-Gusslegierung anhand von zweidimensionalen und dreidimensionalen Verfahren untersucht. Dabei liegt das Hauptaugenmerk auf innenliegenden Gussdefekten wie Gas- und Schrumpfungsporen. Die Schädigungsentwicklung unter schwingender Belastung, sowie der Einfluss auf die Mikrostruktur und die mechanischen Eigenschaften sowie die Wechselwirkung verschiedener Gussdefekte werden dabei untersucht. Insbesondere wird der beim Versagensverhalten entscheidende Einfluss ...
Aufsatz
Hydrogen absorption of ultra-high strength aluminum-silicon coated 22MnB5 steels
(2022-12-30)
The hot forming process allows to produce safety-relevant structural components in the automotive industry with strengths of 1500 MPa and higher. Generally, high strengths make material sensitive to hydrogen embrittlement. The heat treatment in the hot forming process chain is a potential source of diffusible hydrogen for hot-dipped aluminum-silicon coated boron-manganese steels. In the present work, the influence of different process gases and furnace dwell times during the heat treatment was investigated. Humidified ...
Aufsatz
Linking through-thickness cracks in metallic thin films to in-situ electrical resistance peak broadening
(2022-01-29)
Measurements of electrical resistance have been used extensively as a failure criterion in cyclically loaded conductive films. However, not much research has been performed on extracting additional information contained within such resistance data sets. This study shows that an increase in peak width evidences a transition from cracks bridging to through-thickness crack formation. A Au/Cr bilayer system on a polyimide substrate is used for data generation but the method is applicable to any material system where both ...
Aufsatz
Additive Manufacturing of 3D Luminescent ZrO2:Eu3+ Architectures
(2022-04-27)
Implementation of more refined structures at the nano to microscale is expected to advance applications in optics and photonics. This work presents the additive manufacturing of 3D luminescent microarchitectures emitting light in the visible range. A tailor-made organo-metallic resin suitable for two-photon lithography is developed, which upon thermal treatment in an oxygen-rich atmosphere allows the creation of silicon-free tetragonal (t-) and monoclinic (m-) ZrO₂. The approach is unique because the tailor-made ...
Aufsatz
Structural reorientation and compaction of porous MoS₂ coatings during wear testing
(2022-04-02)
Industrial upscaling frequently results in a different coating microstructure than the laboratory prototypes presented in the literature. Here, we investigate the wear behavior of physical vapor deposited (PVD) MoS2 coatings: A dense, nanocrystalline MoS2 coating, and a porous, prismatic-textured MoS2 coating. Transmission electron microscopy (TEM) investigations before and after wear testing evidence a crystallographic reorientation towards a basal texture in both samples. A basal texture is usually desirable due ...
Aufsatz
Microcantilever Fracture Tests of α-Cr Containing NiAl Bond Coats
(2022-01-08)
MCrAlY bond coats are widely used as oxidation-resistant coatings on superalloys. The major phase is the thermally stable intermetallic β-NiAl phase. The addition of Cr increases the oxidation and corrosion resistance but leads to the formation of α-Cr precipitates. Both phases are brittle and limit the fracture toughness of these coatings. To study the influence of thermal exposure and the resulting changing chemical composition on the fracture properties, the fracture toughness of both phases is measured by notched ...
Aufsatz
Investigation of processing windows in additive manufacturing of AlSi10Mg for faster production utilizing data-driven modeling
(2022-04-29)
To reduce production time and decrease production cost, the increase of layer thickness is an adequate option in powder bed fusion. In order to determine the relationships between process parameters in laser powder bed fusion (PBF-LB/M) and final porosity in AlSi10Mg, samples were processed following a space-filling experimental design in the present study. A total of 144 samples were fabricated considering layer thicknesses of 30 µm, 45 µm, 60 µm, and 90 µm. Afterwards, porosity was assessed using image analysis and ...
Aufsatz
Effects of blending poly(lactic acid) and thermoplastic polyester polyurethanes on the mechanical and adhesive properties in two-component injection molding
(2022-09-16)
One possible way to increase the use of bioplastics and thus contribute to a more resource-efficient and sustainable economy is to broaden the application range of such bioplastics. Poly(lactic acid) (PLA) is a promising and commercially available bio-based and biologically degradable polymer, which exhibits a high strength and stiffness but is very brittle. Blending with other polymers can lead to an enhancement of the ductility of the PLA. The goal of this work was to show that blending of PLA with a bio-based ...
Aufsatz
Modification of self-reinforced composites (SRCs) via film stacking process
(2022-02-25)
This work presents the mechanical behavior of self-reinforced composites (SRCs) manufactured and modified via film stacking. For modification, interleaved films made of polypropylene (PP), a thermoplastic elastomer and a polyolefin engage were combined in different ways to induce the elastic modifier into the matrix material. The content of modifier was also varied in two ways. First, the films were produced out of a single material and second out of a compound. So, the same content of modifier was implemented in two ...