Aufsatz
Thermal Stability of Residual Stresses in Differently Deep Rolled Surface Layers of Steel SAE 1045
(2021-05-07)
The stability of compressive residual stresses generated by deep rolling plays a decisive role on the fatigue behavior of specimens and components, respectively. In this regard, deep rolling at elevated temperature has proven to be very effective in stabilizing residual stresses when fatigue analysis is conducted at ambient temperature. However, since residual stresses can be affected not only by plastic deformation but also when thermal energy is provided, it is necessary to analyze the influence of temperature and ...
Aufsatz
Influence of Microstructure and Defects on Mechanical Properties of AISI H13 Manufactured by Electron Beam Powder Bed Fusion
(2021-08-04)
Electron beam powder bed fusion (E-PBF) is a well-known additive manufacturing process. Components are realized based on layer-by-layer melting of metal powder. Due to the high degree of design freedom, additive manufacturing came into focus of tooling industry, especially for tools with sophisticated internal cooling channels. The present work focuses on the relationships between processing, microstructure evolution, chemical composition and mechanical properties of a high alloyed tool steel AISI H13 (1.2344, ...
Aufsatz
On the Impact of Build Envelope Sizes on E-PBF Processed Pure Iron
(2021-11-17)
In additive manufacturing, the thermal history of a part determines its final microstructural and mechanical properties. The factors leading to a specific temperature profile are diverse. For the integrity of a parameter setting established, periphery variations must also be considered. In the present study, iron was processed by electron beam powder bed fusion. Parts realized by two process runs featuring different build plate sizes were analyzed. It is shown that the process temperature differs significantly, ...
Aufsatz
A Novel Thermo-Mechanical Processing Route Exploiting Abnormal Grain Growth in Heusler-Type Co–Ni–Ga Shape Memory Alloys
(2022-10-04)
Heusler-type Co–Ni–Ga shape memory alloys attracted significant scientific attention owing to excellent superelasticity in single-crystalline state. However, due to pronounced anisotropy, polycrystalline Co–Ni–Ga suffers from transformation-induced constraints at grain boundaries and, thus, premature failure upon thermo-mechanical loading. The present study reports on a novel thermo-mechanical processing route. Hot rolling followed by solution-annealing promotes abnormal grain growth, eventually leading to high-performance ...