Characterization of Anisotropic Properties of Hot Compacted Self-Reinforced Composites (SRCs) via Thermal Diffusivity Measurement
(2019-11-01)
The mechanical properties of self-reinforced composites (SRCs) produced in a hot compaction process significantly depend on the process parameters. Only a little deviation of the process temperature or pressure causes the component to act differently under mechanical load. This is a chance and a challenge at the same time, since this process is difficult to handle but by properly controlling the process parameters, the mechanical properties can be adjusted, even locally for one component. In this research SRC are ...
Aufsatz
Joining of Contact Pins and Conductive Compounds via Injection Molding – Influence of the Flow Situation on the Electrical Contact Resistance
(2020-04-09)
While a lot of research can be found in the field of bulk resistance of carbon filled polymers, comparatively few papers focus on contact resistance between compound and metal contacts. Due to that small number of researches that deal with contact resistances, studies of the influence of injection molding conditions and parameters on the contact resistance are also very rare. In contradiction to that, these influences on bulk resistance have been studied. The objective of this work was to investigate the electrical ...
Aufsatz
A Closer Look at the Bonding Capacity of Thick Metal-Plastic Hybrids
(2019-03-01)
Metal-plastic hybrids have a lot of advantages compared to purely metal or purely plastic parts. A good design for metal-plastic hybrids can help to save weight, for example in automotive applications. Therefore, it is important to understand the joining mechanisms between both materials. Aluminum AlSi9Cu3(Fe) and polyamide 6.6 with 35 % glass fibers were used as joining partners. The materials were joined by enclosing the metal part at least partially with plastic right inside the injection molding tool. Afterwards, ...
Aufsatz
UV Pre-Treatment for Polycarbonate for Bonding LSR in a Multi-Component Injection Molding Process
(2019-03-01)
In this study, the influence of UVC radiation and the influence of ozone on the surface energy of specimens made of polycarbonate were investigated. In an additional step, the peeling resistance of silicone flaps, which were overmolded, onto pre-treated PC plates of multicomponent specimens were analyzed. For this purpose, the samples were exposed to UVC radiation for different lengths of time, ranging from 5 s to 3 600 s. To further evaluate the influence of the ozone created by the UVC in the presence of oxygen, ...
Aufsatz
Cross-Linked Hydrophobic Starch Granules in Blends with PLA
(2018-04-17)
The majority of native starch is used in the food sector and in the paper industry. Only a small amount is used in polymer engineering. One reason for the reluctance of the plastics processing industry to use starch as a filling material in polymer blends is the unsatisfactory mechanical behavior of starch when combined with thermoplastics. Another reason is the hydrophilicity of starch. In order to make these materials capable of competing, an amelioration of the mechanical properties is compulsory. By means of ...
Aufsatz
Investigations on Tightness of Polymer-Metal Hybrids in Environments with Thermal, Media, and Mechanical Loads
(2017-07-31)
With polymer-metal hybrids becoming more commonly used as structural components it was investigated how they perform in complex environments with combined thermal, media, and mechanical loads. Special attention was put on media tightness under said loads. This paper sums up the activities of the polymer technology research group of the University of Kassel on hybrids produced by overmolding metal inserts. Investigations concerning joint strength and influence of (cyclic) temperature loads and chemical corrosion on ...
Aufsatz
Mechanical Properties of Polydimethylsiloxane as a Function of the Amount and Type of Crosslinking Agent
(2017-06-13)
In this investigation, a high-consistency rubber (HCR) was mixed with five different, typically used crosslinking agents that are based on organic peroxide. Furthermore, the amount of crosslinking agent was varied in order to quantify the effect on the mechanical properties. All materials were processed in a hot pressing process, and, subsequently, post-cured. The properties were characterized by the measurement of the swelling ratio, shore A-hardness, rebound resilience and tensile test. We successfully proved that ...
Aufsatz
Wood-Polypropylene Composites: Influence of Processing on the Particle Shape and Size in Correlation with the Mechanical Properties Using Dynamic Image Analysis
(2018-11-16)
The particle size and shape are of momentous significance for the mechanical properties of plastic composites. However, natural fillers, like wood, are not consistent in these attributes. In order to investigate the shared traits between these characteristics, WPCs were produced using polypropylene, hardwood and softwood fillers with different particle sizes and a coupling agent. Afterwards, specimens were processed using an injection molding machine. The filler sizes and shapes were measured using dynamic image ...
Aufsatz
![Open Access](/themes/Mirage2/images/Open_Access_logo_PLoS_transparent.svg)
Influence of ethylene oxide and gamma irradiation sterilization processes on the degradation behaviour of poly(lactic acid) (PLA) in the course of artificially accelerated aging
(2024-02-10)
To promote the application of bio-based materials in the field of medical technology, it is essential to conduct additional research, focusing on their long-term performance after sterilization. For this purpose, the study examines the aging behaviour of three poly(lactic-acid) (PLA) materials, sterilized with either ethylene oxide or gamma irradiation, over a two years aging period, in accordance with ASTM F1980-21. During these investigations, a direct correlation between moisture absorption and degradation progression ...