Aufsatz
Electron Beam Welding of Hot-Rolled Fe–Mn–Al–Ni Shape Memory Alloy Sheets
(2023-04-25)
The present study focuses on the weldability of hot-rolled Fe–Mn–Al–Ni shape memory alloy sheets by vacuum electron beam welding. Tailored process-specific welding parameters, such as preheating with electron beam or beam oscillation during welding, allowed defect-free joining with very thin weld seams and heat-affected zones. By applying a post-weld cyclic heat treatment, abnormal grain growth can be promoted across the weld seams. However, regardless of the selected welding parameters, some specimens are characterized ...
Aufsatz
Low-Cycle-Fatigue Performance of Stress-Aged EN AW-7075 Alloy
(2023-05-05)
The effect of a novel heat treatment, that is, aging under superimposed external stress, on the fatigue performance and microstructural evolution of a high-strength aluminum alloy (EN AW-7075) is presented. Stress aging, a combination of heat treatment and superimposed external stress, can enhance the mechanical properties of EN AW-7075 under monotonic loading due to the acceleration of precipitation kinetics. Scanning electron microscopy (SEM) and scanning transmission electron microscopy (STEM) reveal that a longer ...
Aufsatz
Characterization of Mechanical Properties, Macroscopic Deformation Behavior, and Microstructure of Functionally Graded 22MnB5 Steel
(2021-03-24)
The focus of this study is on the characterization of the local plastic deformation and failure of functionally graded 22MnB5 plates after hot stamping using an in situ approach. Various forming strategies at elevated temperatures are performed using differentially tempered forming tools to locally tailor the microstructure. By controlling the cooling rate, graded as well as martensitic and ferritic–pearlitic microstructures are obtained. Experimental analysis includes evaluation of the material- and geometry-dependent ...
Aufsatz
On the Influence of Microstructure on the Corrosion Behavior of Fe–Mn–Al–Ni Shape Memory Alloy in 5.0 wt% NaCl Solution
(2020-10-03)
Herein the corrosion behavior of Fe–Mn–Al–Ni shape memory alloys characterized by different microstructures in a 5.0 wt% NaCl solution is investigated. Open circuit potential and potentiodynamic polarisation tests are conducted. Generally, Fe–Mn–Al–Ni shows corrosion properties being similar to pure iron. However, the polarization curves of single crystals indicate the presence of an unstable passive system. The corrosion damage is analyzed by means of optical microscopy and electron microscopy. It is revealed that ...
Aufsatz
Cooling rate as a process parameter in advanced roll forming to tailor microstructure,mechanical and corrosion properties of EN AW 7075 tubes
(2022-12-14)
The effects of solution heat treatment parameters and quench media as a processing tool for tailoring microstructure, mechanical and corrosion properties in roll forming of EN AW 7075 alloy were studied. The highest yield stress and ultimate tensile strength were obtained for the specimens quenched in water, while the air-cooled specimens exhibited inferior mechanical properties. Microstructural analysis of specimens showed that except water-quenched specimens, the parts cooled/quenched in oil, in direct contact with ...
Aufsatz
UVC Irradiation as a Surface Treatment of Polycarbonate to Generate Adhesion to Liquid Silicone Rubber in an Overmolding Process
(2024-04-18)
This study investigates the adhesion properties of polycarbonate (PC) and liquid silicone rubbers (LSR) through surface activation using ultraviolet C (UVC) radiation. While self-adhesive LSRs adhere easily to certain thermoplastic composites such as polybutylene terephthalate (PBT) and polyamides (PAs), bonding to PC typically requires surface treatment due to the lack of compatible functional groups. Previous methods like plasma or flame treatment have been effective, but the use of UVC radiation for surface ...