Aufsatz
Shape Memory Effect and Superelasticity of [001]-Oriented FeNiCoAlNb Single Crystals Aged under and without Stress
(2021-06-10)
The two-step ageing of Fe-28Ni-17Co-11.5Al-2.5Nb (at.%) single crystals under and without stress, leads to the precipitation of the γ′- and β-phase particles. Research has shown that γ–α′ thermoelastic martensitic transformation (MT), with shape memory effect (SME) and superelasticity (SE), develops in the [001]-oriented crystals under tension. SE was observed within the range from the temperature of the start of MT upon cooling Mₛ, to the temperature of the end of the reverse MT upon heating Af, and at temperatures ...
Aufsatz
The Effect of Fiber Waviness on the Residual Stress State and Its Prediction by the Hole Drilling Method in Fiber Metal Laminates: A Global-Local Finite Element Analysis
(2021-01-15)
In this paper, fiber waviness, as one of the most frequently occurring defects in fiber reinforced composites, is numerically investigated with regard to the formation of residual stresses in fiber metal laminates. Furthermore, the prediction of the residual stress state in the thickness direction by means of the simulated hole drilling method is studied. To this regard, a global-local finite element analysis based on the submodel technique is presented. The submodel technique essentially consists of two governing ...
Aufsatz
Cyclic Crack Growth in Chemically Tailored Isotropic Austenitic Steel Processed by Electron Beam Powder Bed Fusion
(2021-11-01)
The present study analyzes the cyclic crack propagation behavior in an austenitic steel processed by electron beam powder bed fusion (PBF-EB). The threshold value of crack growth as well as the crack growth behavior in the Paris regime were studied. In contrast to other austenitic steels, the building direction during PBF-EB did not affect the crack propagation rate, i.e., the crack growth rates perpendicular and parallel to the building direction were similar due to the isotropic microstructure characterized by ...
Aufsatz
Tribological Performance of Additively Manufactured AISI H13 Steel in Different Surface Conditions
(2021-02-16)
Additive manufacturing of metallic tribological components offers unprecedented degrees of freedom, but the surface roughness of most as-printed surfaces impedes the direct applicability of such structures, and postprocessing is necessary. Here, the tribological performance of AISI H13 steel samples was studied. These were additively manufactured through laser powder bed fusion (L-PBF), also referred to as selective laser melting (SLM). Samples were tested in four different surface conditions: as-printed, polished, ...
Aufsatz
Additive Manufacturing of Compositionally-Graded AISI 316L to CoCrMo Structures by Directed Energy Deposition
(2021-08-30)
In the present study, compositionally-graded structures of AISI 316L and CoCrMo alloy are manufactured by powder-based laser-beam directed energy deposition (DED-LB). Through a process-integrated adjustment of powder flow, in situ alloying of the two materials becomes feasible. Thus, a sharp and a smooth transition with a mixture of both alloys can be realized. In order to investigate the phase formation during in situ alloying, a simulation approach considering equilibrium calculations is employed. The findings ...
Aufsatz
Overmoulding of Additively Manufactured Titanium Inserts Using Polyoxymethylene (POM)—Evaluation of Bond Quality as a Function of Process Parameters
(2021-06-15)
Due to their process-induced porous surfaces, additively manufactured structures are not optimized for applications in which friction is a key factor. To improve the frictional properties of additively manufactured titanium inserts of various thicknesses, two tribologically optimized POM materials, which differ in terms of filler composition and contents, were used to overmould the inserts. The titanium inserts were manufactured in two different building directions, resulting in a variation in surface roughness. The ...
Aufsatz
On the influence of ϰ-carbides on the low-cycle fatigue behavior of high-Mn light-weight steels
(2021)
High-manganese light-weight steels offer a great potential for structural purposes in the mobility sector due to their reduced density combined with outstanding mechanical properties. As many of the envisaged applications of these materials will suffer from cyclic loading during their service life, the fundamentals of their fatigue behavior must be studied extensively. In the present work, the low-cycle fatigue (LCF) properties of an austenitic Fe-29.8Mn-7.65Al-1.11C light-weight steel were investigated. Two ...
Aufsatz
Process Influences in the Combined Compacting and Back-Injection Process to Produce Back-Injected Self-Reinforced Composites (SRCs) – Analysis via Multiple Regression Modelling
(2021-11-21)
A new process to produce back-injected self-reinforced composites (SRCs) is presented. In contrast to other investigations on back-injection of SRCs, a process is presented which allows compacting and back injection of SRCs in one step where the SRCs are partly consolidated only via melt pressure inside the cavity. The mechanical properties of SRCs depend to a large extent on the process parameters of temperature and pressure during manufacture. These parameters are not yet known for back-injected areas. Sensors ...
Aufsatz
On the low-cycle fatigue behavior of thermo-mechanically processed high-strength aluminum alloys
(2021)
In the present work low-cycle fatigue experiments were carried out on thermo-mechanically processed AA6082 and AA7075 sheets to evaluate mechanical properties under cyclic loading. Different cooling rates imposed by use of tempered forming tools after solutionizing and subsequent aging treatment led to the formation of precipitates with differing sizes and morphologies. Specimens thermo-mechanically processed in tools with temperatures of 24 °C and 200 °C showed superior mechanical properties under both monotonic and ...
Aufsatz
Mittelalter erschließen
(2021-07-15)
Research communication has been gaining public attention in recent years. Therefore, medievalists also need to focus on the transfer of their research topics to the public both within and outside the university. Based on current political demands calling for a change in communication culture, the article first of all deals theoretically with two different concepts of research communication, by distinguishing between forms of translation and those of popularization. Numerous public events, exhibitions, and cooperative ...