Aufsatz
Quenching of High Entropy Alloys after Annealing
(2020)
The effect of cooling rate after annealing at 900 °C on the microstructure and hardness of high entropy alloys was investigated using two typical samples with the chemical composition of Co₁₆Cr₁₄.₅Fe₂₉Mn₁₁.₅Ni₂₉ and Co₁₁.₅Cr₇Fe₂₇Mn₂₇Ni₂₇(Nb₀.₀₈C₀.₅) (at%). The microstructural characterisation and hardness measurements were carried out by optical microscopy, scanning electron microscopy, wavelength-dispersive X-ray spectroscopy, electron back scattered diffraction, X-ray diffraction technique and Vickers hardness ...
Aufsatz
Predicting Flow Stress Behavior of an AA7075 Alloy Using Machine Learning Methods
(2022-09-09)
The present work focuses on the prediction of the hot deformation behavior of thermo-mechanically processed precipitation hardenable aluminum alloy AA7075. The data considered focus on a novel hot forming process at different tool temperatures ranging from 24°C to 350°C to set different cooling rates after solution heat-treatment. Isothermal uniaxial tensile tests in the temperature range of 200°C to 400°C and at strain rates ranging from 0.001 s-¹ to 0.1 s-¹ were carried out on four different material conditions. ...
Aufsatz
Effects of Aging under Stress on Mechanical Properties and Microstructure of EN AW 7075 Alloy
(2021-07-20)
In the present study, microstructural and mechanical properties of EN AW 7075 following stress-aging were assessed. For this purpose, properties of stress-aged samples were compared with values obtained for conventionally aged counterparts. It is revealed that the strength and hardness of EN AW 7075 can be increased by the presence of external stresses during aging. Precipitation kinetics were found to be accelerated. The effects of conventional and stress-aging on the microstructure were analyzed using synergetic ...
Aufsatz
Effect of Friction Stir Processing on Microstructural, Mechanical, and Corrosion Properties of Al-Si12 Additive Manufactured Components
(2020-01-03)
Additive manufacturing (AM) is an advanced manufacturing process that provides the opportunity to build geometrically complex and highly individualized lightweight structures. Despite its many advantages, additively manufactured components suffer from poor surface quality. To
locally improve the surface quality and homogenize the microstructure, friction stir processing (FSP) technique was applied on Al-Si12 components produced by selective laser melting (SLM) using two different working media. The effect of FSP on ...
Aufsatz
Novel Class of Rhenium Borides Based on Hexagonal Boron Networks Interconnected by Short B₂ Dumbbells
(2022-09-06)
Transition metal borides are known due to their attractive mechanical, electronic, refractive, and other properties. A new class of rhenium borides was identified by synchrotron single-crystal X-ray diffraction experiments in laser-heated diamond anvil cells between 26 and 75 GPa. Recoverable to ambient conditions, compounds rhenium triboride (ReB₃) and rhenium tetraboride (ReB₄) consist of close-packed single layers of rhenium atoms alternating with boron networks built from puckered hexagonal layers, which link ...
Aufsatz
A new method for microscale cyclic crack growth characterization from notched microcantilevers and application to single crystalline tungsten and a metallic glass
(2022-06-22)
The lifetime of most metals is limited by cyclic loads, ending in fatigue failure. The progressive growth of cracks ends up in catastrophic failure. An advanced method is presented for the determination of cyclic crack growth on the microscale using a nanoindenter, which allows the characterization of > 10,000 loading cycles. It uses focused ion beam fabricated notched microcantilevers. The method has been validated by cyclic bending metallic glass and tungsten microcantilevers. The experiments reveal a stable crack ...
Aufsatz
Mechanics of colloidal supraparticles under compression
(2021-10-13)
Colloidal supraparticles are finite, spherical assemblies of many primary particles. To take advantage of their emergent functionalities, such supraparticles must retain their structural integrity. Here, we investigate their size-dependent mechanical properties via nanoindentation. We find that the deformation resistance inversely scales with the primary particle diameter, while the work of deformation is dependent on the supraparticle diameter. We adopt the Griffith theory to such particulate systems to provide a ...
Aufsatz
Exploring the mechanical properties of additively manufactured carbon-rich zirconia 3D microarchitectures
(2023-07-11)
Two-photon lithography (TPL) is a promising technique for manufacturing ceramic microstructures with nanoscale resolution. The process relies on tailor-made precursor resins rich in metal–organic and organic constituents, which can lead to carbon-based residues incorporated within the ceramic microstructures. While these are generally considered unwanted impurities, our study reveals that the presence of carbon-rich residues in the form of graphitic and disordered carbon in tetragonal (t-) ZrO₂ can benefit the ...
Aufsatz
Describing mechanical damage evolution through in situ electrical resistance measurements
(2023-02-27)
The fatigue properties of metallizations used as electrical conductors in flexible electronic devices have been thoroughly studied over the years. Most studies use time-intensive characterization methods to evaluate mechanical damage. For their ease of access, in situ electrical resistance measurements are often performed along with other characterization methods. However, the data are mostly used as an indicator of failure and a thorough analysis is usually missing. This work presents some deeper analysis methods ...
Aufsatz
Linking through-thickness cracks in metallic thin films to in-situ electrical resistance peak broadening
(2022-01-29)
Measurements of electrical resistance have been used extensively as a failure criterion in cyclically loaded conductive films. However, not much research has been performed on extracting additional information contained within such resistance data sets. This study shows that an increase in peak width evidences a transition from cracks bridging to through-thickness crack formation. A Au/Cr bilayer system on a polyimide substrate is used for data generation but the method is applicable to any material system where both ...